Uncured
Properties - Resin [Part A] |
|
|
41,100 cps |
Specific
Gravity |
|
1.8019 |
Color |
|
Black |
Uncured
Properties - Hardener [Part B] |
|
|
68,900 cps |
Specific
Gravity |
|
1.5036 |
Color |
|
Black |
Cured
Properties - PHYSICAL |
Test Method |
|
Mixed
|
|
76,300 cps |
Mixed
Specific Gravity |
|
1.6156 |
Volume
Mix Ratio (resin:hardener) |
|
1:1 |
Working
time (100g) |
|
120 min. |
Cure
Time (100g, room temp.) |
|
48 hours |
Heat
Cure Time (100g, 65°C) |
|
60 min. |
Shore Hardness |
|
82 Shore D |
Tensile strength |
ASTM-D-638-02A |
2734 psi |
Elongation |
ASTM-D-638-02A |
1.87 % |
Compressive Strength |
ASTM-D-695-02A |
4,088 psi |
Flexural Strength |
ASTM-D-790-03 |
5,352 psi |
Cantilever Beam (IZOD) Impact |
ASTM-D-256-02 E1 |
0.80 ft lb ft / in |
Shear Strength |
ASTM-E-831-03 |
3.224 psi |
Cured
Properties - TEMPERATURE |
Test Method |
|
Constant
Service Temperature |
|
90°C (194°F) |
Heat Deflection Temperature |
ASTM-D-648-01 |
35.35°C (95.6°F) |
Dielectric Constant |
ASTM-D-150-98 |
4.41 |
Dissipation Factor |
ASTM-D-150-98 |
0.0113 |
Volume Resistivity |
ASTM-D-257-99 |
2.58 x 1015 ohm · cm |
Surface Resistivity |
ASTM-D-257-99 |
3.16 x 1016 ohm · cm |
Heat Deflection Temperature |
ASTM-D-648-01 |
35.35°C (95.6°F) |
Intermediate
Service Temp. |
|
110°C (230°F) |
Thermal
Conductivity |
|
0.682 W/m*K |
Thermal
Diffusivity |
|
0.38 mm2/s |
Volumetric
Specific Heat |
|
1.9MJ/m3*K |
Thermal Expansion |
ASTM-E-831-03 |
148.3x10-6 mm/mm°C |
Chemical
and Solvent Resistance |
|
Change after 3 days: |
Hydrocloric
Acid |
|
|
Isopropyl
Alcohol |
|
~ 0% |
Ethyl
Lactate |
|
|
Acetone |
|
|
Xylene |
|
|
Iso
hexanes |
|
~ 0% |
Mineral
spirits |
|
~ 0% |